344 F.3d 1234 | Fed. Cir. | 2003
Lead Opinion
Opinion for the court filed by Circuit Judge LOURIE. Concurring opinion filed by Circuit Judge RADER. AK Steel Corporation appeals from the decision of the United States District Court for the Southern District of Ohio granting summary judgment that its U.S. Patent 4,800,135 was not infringed by Sol-lac and Ugine (collectively, “Sollac”) and that certain claims of its U.S. Patent 5,066,549 are invalid. AK Steel Corp. v. Sollac, 234 F.Supp.2d 711 (S.D.Ohio 2002). Because the court properly construed the patent claims and correctly found no genuine issues of material fact, we affirm.
BACKGROUND
AK Steel owns the '135 and '549 patents, which are directed to hot-dip aluminum-coated stainless steel. The '549 patent issued from an application that was a continuation of the application from which the '135 patent issued. As such, the two patents have different claims but share a common specification. That specification explains that aluminum-coated stainless steel has desirable resistance to corrosion and high-temperature oxidation. '135 patent, col. 1, 11. 14-23. Those properties make such steel useful in the manufacture of components for use in automotive exhaust systems and combustion equipment. Id. Hot-dip aluminum-coated steel is produced by passing heated steel strips through molten aluminum; however, it is challenging to get the aluminum to adhere or “wet” well onto the steel. Id. at col. 2, 11. 21-25. Wetting problems can result in crazing or flaking of the aluminum coating during subsequent bending of the strip. Id. at col. 2, 11. 26-27. The inventors of the patents in suit solved the wetting problem by maintaining the steel strip in a hydrogen atmosphere prior to entry into the aluminum coating bath. Id. at col. 2, 11. 44-50.
The inventors also discovered that their invention did not work well unless the aluminum is substantially pure, as they stated in their patent application:
Most hot dip aluminum coatings contain about 10% by weight silicon. This coating metal is generally defined in the industry as Type 1. We have discovered this type aluminum coating metal does not wet well with ferritic chromium alloy steel, even when using the hydrogen protective atmosphere. While not being bound by theory, it is believed silicon exceeding 0.5% by weight decreases the reactivity of the aluminum coating metal needed to react with a ferritic chromium alloy steel substrate. Accordingly, silicon contents in the coating metal should not exceed about 0.5% by weight.
*1237 Commercially pure hot dip aluminum coatings, otherwise known as Type 2 in the industry, are preferred for our invention. By “pure” aluminum is meant those aluminum coating metals where addition of substantial amounts of alloying elements, such as silicon, are precluded.
Id. at col. 5,11. 23-40 (emphases added).
The '135 patent, the first of the two patents chronologically, contains one independent claim, which reads as follows:
1. A ferrous base ferritic strip continuously hot dip coated with a coating metal; comprising: the strip including at least about 6% by weight chromium, the coating metal consisting essentially of aluminum, the coating layer on said strip being substantially free of uncoat-ed areas and formed without a thick brittle Fe-Al alloy inner layer,
said coating layer being tightly adherent to said strip and resistant to crazing or flaking during bending.
Id. at col. 6, 1. 62 to col. 7, 1. 2 (emphasis added). The pertinent limitation of that claim, as emphasized above, is that the coating “consistí ] essentially of aluminum.”
The application from which the '549 patent issued was filed as a continuation of the application from which the '135 patent issued. In that continuation application, the inventors sought and obtained broader claims. Rather than require that the coating metal consist essentially of aluminum, the independent claims of the '549 patent require that the coating metal include “aluminum or aluminum alloys” or simply have enhanced wetting characteristics. '549 patent, col. 7,11. 1-7; col. 8,11. 5-9. Of the eight claims in the '549 patent, only the odd-numbered ones are at issue in this appeal; they read as follows:
1. A ferrous base ferritic strip continuously hot dip coated with a coating metal, comprising:
the strip including at least about 6% by weight chromium,
the coating metal including aluminum or aluminum alloys,
the coating layer on the strip being substantially free of uncoated areas and formed without a thick brittle Fe-Al alloy inner layer,
the coating layer being tightly adherent to the strip and resistant to crazing or flaking during bending.
3. The strip of claim 1 wherein the aluminum coating metal contains up to about 10% by weight silicon.
5. A ferritic steel strip continuously hot dip coated with an aluminum coating metal, comprising:
the strip being stainless steel including at least about 10% by weight chromium,
the coating layer on the strip being substantially free of uncoated areas and formed without a thick brittle Fe-Al alloy inner layer,
the coating layer being tightly adherent to the strip and resistant to crazing or flaking during bending.
7. The strip of claim 5 wherein the aluminum coating metal contains up to about 10% by weight silicon.
Id. at col. 6,1. 65 to col. 7,1. 7; col. 8,11. 1-9,12-13 (emphases added).
The independent claims 1 and 5 were allowed by the Patent and Trademark Office (“PTO”) without amendment or alteration. However, when the dependent claims 3 and 7 were originally filed, rather than reciting that “the aluminum coating contains up to about 10% by weight silicon,” they read “the coating metal is Type 1 aluminum.” The examiner rejected both claims under 35 U.S.C. § 112, ¶ 2, as being
AK Steel sued Sollac in the district court for infringement of several patents, including the '135 and '549 patents. Sollac manufactures stainless steel that is hot-dipped in a molten mixture including aluminum and 8.0%-8.5% silicon.
The district court judge adopted a special master’s construction of the phrase “consisting essentially of aluminum” in the '135 patent claims to permit no more than “about 0.5% silicon” and therefore granted summary judgment of noninfringement. AK Steel, 234 F.Supp.2d at 720. The judge also adopted the special master’s thorough construction of claims 1, 3, 5, and 7 of the '549 patent as encompassing Type 1 aluminum and his conclusion that the patent did not enable one skilled in the art to practice the invention with Type 1 aluminum, as required by 35 U.S.C. § 112, ¶ 1 .Id. at 718. The court therefore granted summary judgment of invalidity with respect to those '549 patent claims. Id. at 719. AK Steel timely appealed and Sollac timely cross-appealed to this court. We have jurisdiction pursuant to 28 U.S.C. § 1295(a)(1).
DISCUSSION
We review a district court’s grant of a motion for summary judgment de novo. Ethicon Endo-Surgery, Inc. v. U.S. Surgical Corp., 149 F.3d 1309, 1315 (Fed.Cir.1998). Summary judgment is appropriate if “there is no genuine issue as to any material fact and ... the moving party is entitled to a judgment as a matter of law.” Fed.R.Civ.P. 56(c). “The evidence of the nonmovant is to be believed, and all justifiable inferences are to be drawn in his favor.” Anderson v. Liberty Lobby, Inc., 477 U.S. 242, 255, 106 S.Ct. 2505, 91 L.Ed.2d 202 (1986). Furthermore, in deciding whether summary judgment is warranted, the court “must view the evidence presented through the prism of the substantive evidentiary burden” that would inhere at trial. Id. at 245, 106 S.Ct. 2505.
A determination of patent infringement requires a two-step analysis. “First, the court determines the scope and meaning of the patent claims asserted ... [Second,] the properly construed claims are compared to the allegedly infringing device.” Cybor Corp. v. FAS Techs., Inc., 138 F.3d 1448, 1454 (Fed.Cir.1998) (en banc) (citations omitted). Step one, claim construction, is an issue of law, Markman v. Westview Instruments, Inc., 52 F.3d 967, 970-71 (Fed.Cir.1995) (en banc), aff'd, 517 U.S. 370, 116 S.Ct. 1384, 134 L.Ed.2d 577 (1996), that we review de novo, Cybor, 138 F.3d at 1456. Step two, comparison of a claim to the accused device, requires a determination that every claim limitation or its equivalent is found in the accused device. Warner-Jenkinson Co. v. Hilton Davis Chem. Co., 520 U.S. 17, 29,117 S.Ct. 1040, 137 L.Ed.2d 146 (1997). Those determinations are questions of fact. Bai v. L & L Wings, Inc., 160 F.3d 1350, 1353 (Fed.Cir.1998).
Whether the subject matter of a patent claim satisfies the enablement requirement of 35 U.S.C. § 112, ¶ 1, is a question of law based on underlying facts, In re Wands, 858 F.2d 731, 735 (Fed.Cir.1988), and, because a patent is presumed to be valid, 35 U.S.C. § 282 (2000), the evidentiary burden to show facts support
On appeal, AK Steel argues that the court erred by interpreting the '135 patent claims too narrowly and the '549 patent claims too broadly. It contends that the claims of both patents should be construed to cover coating baths containing up to, but not including, 10% silicon. Under that claim construction, according to AK Steel, there are genuine issues of material fact relating to infringement of the '135 patent claims and enablement of the '549 patent claims.
Sollac responds that the court correctly construed both patents’ claims and properly found no genuine issue of material fact as to noninfringement of the '135 patent claims and lack of enablement of the involved '549 patent claims. Sollac also cross-appeals, arguing that the court abused its discretion in denying it summary judgment of invalidity of the same '549 patent claims on the grounds of lack of written description and anticipation by AK Steel’s earlier U.S. Patent 4,675,214. The district court adopted the special master’s recommendation to deny summary judgment of invalidity for lack of written description and not to decide the anticipation issue.
A. The '135 Patent
AK Steel argues that the district court erred in interpreting the phrase “consisting essentially of aluminum” in the '135 patent claims to permit only up to about 0.5% silicon. Rather, according to AK Steel, the correct interpretation permits silicon in an amount up to but not including 10%, as the intrinsic evidence shows that about 10% silicon materially changes the novel characteristics of the invention. AK Steel contends that the court read the specification’s statement that “silicon should not exceed about 0.5%” out of context. That statement, which advanced a theory that the applicants expressly stated was not binding on them, relates to reactivity, according to AK Steel, not to the critical characteristic of the claimed invention—good wetting.
Sollac responds that the specification clearly states that the invention is to be used with pure or nearly pure aluminum and should not be used with Type 1 aluminum. Sollac further contends that the prosecution history also contains statements expressing that view. Finally, Sol-lac contends that, given the choice between a broader and narrower construction, and the enablement concerns raised by the broader one, the narrower one should prevail.
We agree with the district court’s construction of the disputed claim language. The phrase “consisting essentially of’ in a patent claim represents a middle ground between the open-ended term “comprising” and the closed-ended phrase “consisting of.” In view of the ambiguous nature of the phrase, it has long been understood to permit inclusion of components not listed in the claim, provided that they do not “materially affect the basic and novel properties of the invention.” PPG Indus. v. Guardian Indus. Corp., 156 F.3d 1351, 1354 (Fed.Cir.1998); In re Janakirama-Rao, 50 C.C.P.A. 1312, 317 F.2d 951, 954 (CCPA 1963). Thus, the claim construction issue presented by the '135 patent in this case is whether an amount of silicon in excess of 0.5% in the aluminum coating materially affects the basic and novel properties of the invention.
To determine those properties, we need look no further than the patent specification. The specification clearly states that good wetting is the goal of the invention as
AK Steel’s attempt to distance itself from the clear limiting statements in its specification is unavailing. While it is true that statements in a specification explaining a scientific theory by which an invention is believed to operate should seldom, if ever, be treated as a limitation on a claimed invention, e.g., Fromson v. Advance Offset Plate, Inc., 720 F.2d 1565, 1570 (Fed.Cir.1983), the district court did not do so here. There is a distinction between an inventors’ theory as to the reason for a limitation and the meaning of that limitation. By its very terms, the specification here expresses the inventors’ desire not to be bound by the reactivity theory they present to explain why aluminum with more silicon does not wet well. See '135 patent, col. 5, 11. 29-34 (“While not being bound by theory....”). However, no such disclaimer attaches to the following conclusion that silicon should not exceed 0.5%. That conclusion is not a theory; it is an expression speaking to the conditions under which the invention will or will not operate properly. As such, AK Steel cannot escape its impact upon the meaning of the claim phrase “consisting essentially of aluminum.”
Nor are we persuaded by AK Steel’s arguments that the determination whether more than 0.5% silicon materially alters the basic and novel properties of the invention is a question of fact that must be answered by the jury. While “consisting essentially of’ language in a patent claim can at times blur the distinction between the separate steps in an infringement analysis (claim construction and comparison of the construed claim to the accused device or method), the distinction is clear enough in this case. AK Steel cites PPG Industries to support its position that that determination is a factual one for the jury. Indeed, we held in that case that “[t]he court properly left it to the jury to determine whether the amounts of iron sulfide in [the accused] SMG glass have a material effect on the basic and novel characteristics of the glass.” Id. However, we so held there because, as we stated in the immediately preceding sentence, “The district judge properly recognized that the patent is silent about iron sulfide and about what constitutes a material effect on the properties of the glass.” Id. In this case, quite differently, the specification is far from silent regarding silicon and its material effect on the properties of the aluminum coating bath and the resultant coated steel; as explained above, the specification directly speaks to and conclusively answers that question. Therefore, it is as a matter of claim construction that we hold that the claims of the '135 patent do not encompass steel coated with aluminum containing
B. The '519 Patent
We next turn to the '549 patent and the question whether the court correctly granted summary judgment that the contested claims of that patent are not enabled. Because a patent specification must enable the full scope of a claimed invention, In re Wright, 999 F.2d 1557, 1561 (Fed.Cir.1993), an enablement inquiry typically begins with a construction of the claims, see MPEP § 2164.08 (8th ed., rev.1-2003) (“All questions of enablement are evaluated against the claimed subject matter. The focus of the examination inquiry is whether the substantial scope of the claim is enabled. Accordingly, the first analytical step requires that the examiner determine exactly what subject matter is encompassed by the claims.”).
1. Claim Construction
AK Steel argues that the district court’s construction of the '549 patent claims as including Type 1 aluminum is contrary to (1) the ordinary meaning of “up to” as not including the 10% endpoint; (2) the claims’ recitation that the coating must wet well; (3) the specification’s clear disclaimer of Type 1 aluminum; and (4) the axiom that claims should be interpreted to preserve their validity. According to AK Steel, the court mistakenly assumed that the applicants did not narrow the claims when they replaced the words “Type 1 aluminum” with “up to about 10%” silicon, when in fact they did so to surrender that subject matter.
Sollac responds that AK Steel’s dictionary definition of “up to” is nonsensical where a numerical limit follows that phrase. In such a case, according to Sol-lac, the limit is included (e.g., counting up to ten stops at ten, not nine). Sollac also contends that the amendment replacing “Type 1” with “up to about 10%” was presented as an improvement in clarity, not as an exclusion of subject matter. Moreover, the amendment affected only the dependent claims, not the independent claims, which were submitted with an explanation that they encompass any type of aluminum.
We agree with Sollac as to the meaning of the '549 patent claims. We begin with the dependent claims 3 and 7. Those claims state that the silicon content of the aluminum coating is “up to about 10%.” '549 patent, col. 7, 1. 11; col. 8, 1. 13. We hold that those claims do indeed extend up to, and include, 10% silicon in the aluminum coating, i.e., Type 1 aluminum coatings.
First, we conclude that the ordinary meaning of the phrase “up to about 10%” includes the “about 10%” endpoint. As pointed out by AK Steel, when an object of the preposition “up to” is nonnumeric, the most natural meaning is to exclude the object (e.g., painting the wall up to the door). On the other hand, as pointed out by Sollac, when the object is a numerical limit, the normal meaning is to include that upper numerical limit (e.g., counting up to ten, seating capacity for up to seven passengers). Because we have here a numerical limit — “about 10%” — the ordinary meaning is that that endpoint is included.
Moreover, the prosecution history shows that the phrase was introduced into the claims with the intention and effect of covering the endpoint. Claims 3 and 7 origi
Turning next to the independent claims, we begin their interpretation by analyzing their ordinary meaning. According to their plain language, independent claim 1 permits the coating metal to include any “aluminum or aluminum alloy,” id. at col. 7, 11. 1-2, while independent claim 5 does not contain any express limitation regarding the composition of the coating metal, other than that it be “an aluminum coating metal,” id. at col. 8,1. 2. The ordinary meaning of those phrases in claims 1 and 5, then, is that they encompass a metal coating mixture of aluminum, including perhaps a significant amount of silicon. We need not determine the upper limit, if any, of silicon that the claim language permits, but the claims must cover up to at least 10% silicon, as the parties do not dispute that a mixture of about 10% silicon and approximately 90% aluminum is an “aluminum alloy” and “an aluminum ... metal.” Id. at col. 7,11.1-2; col. 8,1. 2.
Moreover, and most importantly, claims 1 and 5 must also encompass aluminum with up to about 10% silicon, ie., Type 1 silicon, because claims 3 and 7, which depend from claims 1 and 5, respectively, expressly recite “up to about 10% silicon.” Under the doctrine of claim differentiation, dependent claims are presumed to be of narrower scope than the independent claims from which they depend. See RF Del, Inc. v. Pac. Keystone Techs., Inc., 326 F.3d 1255, 1264 (Fed. Cir.2003) (stating that an independent claim is usually accorded a scope greater than its dependent claims); see also 35 U.S.C. § 112, ¶4 (2000) (“[A] claim in dependent form shall contain a reference to a claim previously set forth and then specify a further limitation of the subject matter claimed. A claim in dependent form shall be construed to incorporate by reference all the limitations of the claim to which it refers.”). That presumption is applicable in this case and has not been rebutted. If the dependent claims expressly recite “up to about 10%” silicon, then the independent claims, which must be at least as broad as the claims that depend from them, must include aluminum coatings with “up to about 10%” silicon. Independent claims 1 and 5 therefore also cover at least steel strips hot-dip coated with aluminum containing about 10% silicon, ie., Type 1 aluminum.
AK Steel’s remaining arguments concerning the interpretation of the claims are unpersuasive. First, AK Steel points to language in the independent claims describing the functional qualities of the coating layer, ie., “being substantially free of uncoated areas,” “formed without a thick brittle Fe-Al alloy inner layer,” and “being tightly adherent to the strip and
AK Steel’s contention that a narrower construction of the '549 patent claims is in order under the axiom that claims should be interpreted to preserve their validity when possible is also unpersuasive. That axiom is a qualified one, dependent upon the likelihood that a validity-preserving interpretation would be a permissible one. In this case, the interpretation advocated by AK Steel, while possibly avoiding validity pitfalls, cannot be a correct interpretation, for it is counter to the ordinary meaning of the claims as well as to the prosecution history.
We recognize that we have interpreted differently two similar claims supported by the same specification. We are holding that one set of claims is limited to 0.5% silicon; the other, up to and including about 10%. Such a situation may be regarded as unusual. However, that is a necessary consequence of the clear statements in the specification, as applied to the '135 patent claims, and the fact of claim dependency and the prosecution history, as applied to the '549 patent. The '135 patent claims also contain the narrowing term “consisting essentially of,” which is not in the '549 patent claims. Thus, our differing constructions of the two patents’ claims is compelled by all of the relevant facts.
2. Enablement
Given our construction of the '549 patent claims, we turn to the question whether the district court properly determined that those claims have not been enabled.
AK Steel principally argues that the court’s enablement holding was premised on a faulty claim construction, a point we have already rejected. AK Steel further contends that Sollac failed to submit any evidence — let alone clear and convincing evidence — of undue experimentation, and that AK Steel is entitled to the presumption of validity, which it contends is especially weighty. Finally, AK Steel contends that the patent discloses several embodiments within the properly construed claim range, and that the patent specification need not teach the full claimed range in order for the claims to be enabled.
Sollac responds that under the court’s construction of the '549 patent claims, they are not enabled in their full scope. As evidence of nonenablement, Sollac points to the statements in the specification itself, as well as AK Steel’s own documents and testimony from its personnel reflecting their inability to use 9% silicon Type 1 aluminum effectively.
We agree with the district court that the claims as construed have not been enabled. The enablement requirement is set forth in the first paragraph of section 112 of title 35, which provides in pertinent part that the specification shall describe “the manner and process of making and
As we have stated, all of the contested '549 patent claims read on steel strips containing either a Type 1 or a Type 2 aluminum coating. Furthermore, the claims require that the coating wet well. The specification undoubtedly enables the invention in the latter form, as it clearly describes how to make and use such strips with Type 2 aluminum, and there is no question that the resulting strips are well-wetted. However, as part of the quid pro quo of the patent bargain, the applicant’s specification must enable one of ordinary skill in the art to practice the full scope of the claimed invention. Wright, 999 F.2d at 1561. That is not to say that the specification itself must necessarily describe how to make and use every possible variant of the claimed invention, for the artisan’s knowledge of the prior art and routine experimentation can often fill gaps, interpolate between embodiments, and perhaps even extrapolate beyond the disclosed embodiments, depending upon the predictability of the art. See Genentech, Inc. v. Novo Norilsk A/S, 108 F.3d 1361, 1366 (Fed.Cir.1997) (“[A] specification need not disclose what is well known in the art.”); see also Wands, 858 F.2d at 736-37 (“Enablement is not precluded by some experimentation, such as routine screening.”). But it does mean that, when a range is claimed, there must be reasonable enablement of the scope of the range. The question more precisely here is whether, with AK Steel’s patent specification as an initial guide, the hypothetical skilled artisan’s knowledge of the surrounding art and ability to modestly experiment would have been sufficient to enable him to make and use a steel strip containing a Type 1 aluminum coating, with the claimed wetting attributes, at the time of the '549 patent’s effective filing date in 1986.
We conclude that the specification is inadequate as a matter of law in that regard primarily because it expressly teaches against it. Worse than being silent as to that aspect of the invention, the specification clearly and strongly warns that such an embodiment would not wet well. In particular, the specification warns that silicon content above 0.5% in the aluminum coating causes coating problems. Such a statement discourages experimentation with coatings having more than 0.5% silicon, undue or otherwise. It tells the public that higher amounts of silicon will not work. Nothing further need be said about the matter.
Moreover, we disagree with AK Steel’s contention that Sollac failed to submit evidence that undue experimentation would be required to enable practice of the claims. Sollac presented documentary and testimonial evidence from AK Steel that despite its desire to utilize a Type 1 aluminum coating, it was unable to do so at the time of the effective filing date. AK Steel, 234 F.Supp.2d at 782-83. Furthermore, as explained above, the specification’s teaching is itself evidence that at least a significant amount of experimentation would have been necessary to practice the claimed invention utilizing Type 1 aluminum. In summary, given the specification’s teaching away from the subject matter that was eventually claimed and AK Steel’s own failures to make and use the later claimed invention at the time of the application, the district court correctly concluded that there was no genuine issue of
Finally, we dispel the notion that the failure of the PTO to issue an enablement rejection automatically creates an “especially weighty presumption” of compliance with 35 U.S.C. § 112. AK Steel cites language in Brooktree Corp. v. Advanced Micro Devices, Inc., 977 F.2d 1555, 1574-75 (Fed.Cir.1993), to that effect. However, whether a patent complies with the enablement requirement depends upon a factually intensive inquiry regarding the amount of experimentation required, see Wands, 858 F.2d at 737, an issue to be evaluated on a case-by-case basis. Indeed, the presumption is far from determinative, and we have on occasion invalidated patent claims as not having been enabled, despite the PTO’s having allowed those claims. Kg., Genentech, 108 F.3d at 1368. This is another such case. The specification here itself plainly tells us that use of aluminum up to about 10% silicon is not enabled.
To conclude, the specification does not enable a significant portion of the subject matter encompassed by the contested claims of the '549 patent, as properly construed. Accordingly, we affirm the district court’s judgment of invalidity of those claims on the ground of noncompliance with 35 U.S.C. § 112, ¶ 1.
3. Cross-Appeal
Finally, because we affirm the court’s judgment that the contested claims of the '549 patent are invalid, we need not reach Sollae’s cross-appealed issues, which are alternative grounds for reaching the same judgment.
CONCLUSION
Because the court correctly construed the claims of the '135 and '549 patents, and there are no genuine issues of material fact disentitling AK Steel to summary judgments of noninfringement and invalidity, respectively, as a matter of law, we
AFFIRM.
Concurrence Opinion
concurring.
While I endorse the results and reasoning of the majority, I write separately to present an alternative reason for concluding that contested claims 1, 3, 5, and 7 of the '549 patent are invalid. This court sustained the district court’s determination that those claims were invalid for lack of an enabling disclosure. The district court declined to reach a point raised by the special master, namely that prior art anticipated those claims. The record suggests that the special master was correct.
In this case, the prior art is the '549 patent’s grandparent U.S. Patent No. 4,675,214 (the '214 patent). The '549 patent is the third in a group of related patents with identical disclosures. The '214 patent was the first in that series. The '214 patent as filed disclosed that “silicon contents in the coating metal should not exceed about 0.5% by weight.” '214 patent, col. 5, 11. 30-31. The later '549 patent recites in the contested claims a coating metal containing “aluminum,” “aluminum alloys,” or “up to about 10% by weight silicon.” Thus, the later '549 patent added new matter to the original disclosure. Specifically, the later patent claimed much higher concentrations of silicon. Because the specification of the '214 patent as filed contains no support for this new matter, the applicant cannot claim priority back to the filing date of the earlier application that matured into the '214 patent.
Thus, when an applicant files continuation applications, a patent issuing from an earlier application may anticipate claims containing new matter under 35 U.S.C. § 132. When the earlier application lacks any support in the written description for the new subject matter, the new matter cannot claim priority back to the original filing. In that case, a patent issuing from the earlier application may become anticipatory prior art, as occurred here.
. For the same reason, the contested claims do not benefit from the filing date of the intermediate '135 patent.